| About |
|---|
| BITONER BT-2104 is thermoplastic, low molecular weight, slightly yellow aliphatic resin obtained from petroleum-derived monomers.Characterized by low molecular weight,narrow MWD,low wax cloud point, good compatibility with APP, APAO, Natural Rubber,SIS,Butyl Rubber and other polymers,this grade is mainly used in PSA,Hot Melt Adhesive and Sealants. Characteristics: Excellent compatibility with SIS,and other polymers Good thermal stability Low Molecular Weight and Narrow MWD Low Wax Cloud Point Low volatility and low odor Water resistance Applications: HMPSA Solvent based PSA Hot Melt Adhesive Sealants&& |
| Product Description | |
|---|---|
| Supplier | Bater |
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Low or no water absorption,Low odor,Aliphatic series,Weight distribution,Low molecular weight,Heat Stabilized |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Glass transition temperature | 55.0 | ℃ | |
| Softening temperature | 95 to 105 | ℃ | ASTM E28 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.920 to 0.990 | g/cm³ | Internal Method |
| acid value | < 0.30 | Mg KOH/g | ASTM D974 |
| colour | |||
| 50% resin solid in Toluene | Max4# | ASTM D1544 | |
| Apparent viscosity of melt | |||
| 175℃ | < 500 | mPa·s | ASTM D3236 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. midpoint |
| 3. Ring & Ball |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |