| About |
|---|
| TC-1607 A/B is an unfilled, medium viscosity laminating resin for high temperature plastic tooling and part fabrication. This system is ideal for wet lay-up tooling applications where excellent dimensional stability and high mechanical properties are required. Features: Easy to use for lay-ups requiring vacuum bagging Withstands temperatures to 350°F (177°C) Designed for fabrication nof a variety of molds&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Density | |||
| Part A | 1.200 | g/cm³ | |
| Part B | 1.000 | g/cm³ | |
| Shrinkage rate | 0.13 | % | |
| viscosity | |||
| blend | 2.10 | Pa·s | |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Laminate Service Temperature | 177 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore D, 177 ℃ | 87 | ||
| Shaw’s D, 25 ℃ | 95 | ||
| tensile strength | 176 | MPa | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 25℃ | 15500 | MPa | |
| 177℃ | 6890 | MPa | |
| bending strength | ASTM D790 | ||
| 25℃ | 335 | MPa | |
| 177℃ | 103 | MPa | |
| compressive strength | 182 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 166 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-5 | 1/℃ | ASTM D3386 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 100 | ||
| Component B | 按重量计算的混合比: 20 | ||
| Storage period | 52 | wk | |
| stripping time | 1.0 | day | |
| working hours | |||
| 25℃ | 35.0 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part B, 77°F |
| 3. Part A, 77°F |
| 4. 16 plies of 7500 fiberglass cloth laid up at 0° and 45° |
| 5. Mixed |
| 6. Part B |
| 7. Part A |
| 8. 1 lb mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |