BJB Polyurethane TC-8750 A/B

About
TC-8750 A/B is a two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use casting highly wear-resistant parts and linings. This product is safe and easy-to-handle. TC-8750 A/B is relatively insensitive to typical environmental moisture and will make excellent void-free parts without the problems that some conventional urethane systems exhibit. Because of this product’s exceptional toughness and abrasion resistance, castings made with TC-8750 A/B are particularly suitable for mining and mineral process industries. Product Highlights: Exceptionally tough, abrasion resistant, high impact material Contains no MDI, MDA, OR MOCA Easy to handle Room temperature mixing and curing&&

About

TC-8750 A/B is a two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use casting highly wear-resistant parts and linings. This product is safe and easy-to-handle. TC-8750 A/B is relatively insensitive to typical environmental moisture and will make excellent void-free parts without the problems that some conventional urethane systems exhibit. Because of this product’s exceptional toughness and abrasion resistance, castings made with TC-8750 A/B are particularly suitable for mining and mineral process industries. Product Highlights: Exceptionally tough, abrasion resistant, high impact material Contains no MDI, MDA, OR MOCA Easy to handle Room temperature mixing and curing&&

Product Description
Generic	TSU
Material Status	Commercial: Active
Features	High impact resistance,Ultra high toughness,Good wear resistance
Availabilitys	North America
Process Methods	casting

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density
—	1.12	g/cm³
—	1.17	g/cm³
—	1.13	g/cm³	ASTM D792
Shrinkage rate	0.20	%	ASTM D2566

elastic body	Nominal value	Unit	Test method
tensile strength
yield	20.7	MPa	ASTM D412
Tensile strain
fracture	450	%	ASTM D412
tear strength	105	kN/m	ASTM D624

THERMAL	Nominal value	Unit
Thermosetting components
Component A	按重量计算的混合比: 100, 按容量计算的混合比: 100
Component B	按重量计算的混合比: 30, 按容量计算的混合比: 29
Storage period
25℃	26	wk

Thermosetting mixed viscosity	Nominal value	Unit
25℃	4000	cP
25℃	250	cP
25℃	4750	cP
stripping time
25℃	240 to 360	min
Gelation time	20.0	min
working hours
25℃	15.0	min

Supplementary information	Nominal value	Unit	Test method
Curing time
25℃	5.0 to 7.0	day

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	50 to 60		ASTM D2240
Bending modulus	173	MPa	ASTM D790
bending strength	6.69	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.