| TC 5005 A/B-C is a room temperature curing silicone elastomer intended primarily for making silicone skins, but is also used as a general purpose rubber. This product is a condensation cured system using a tin catalyst that provides a 1.5-2 hour work time with 16-24 hour demold time. Product Highlights: Low viscosity and easily poured Perfect for skin simulation Translucent in color High elongation&& |
| Product Description | |
|---|---|
| Generic | 硅酮 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,High Heat Resistance,Good Tensile Strength |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 0.968 | g/cm³ | |
| — | 0.988 | g/cm³ | |
| — | 1.09 | g/cm³ | |
| — | 1.05 | g/cm³ | ASTM D792 |
| Shrinkage rate | Negligible | ASTM D2566 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s OO | 5 to 15 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 0.938 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 700 | % | ASTM D412 |
| tear strength | 2.28 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 100 | ||
| Component B | 按重量计算的混合比: 10 | ||
| Storage period | 26 | wk | |
| Thermosetting mixed viscosity | Brookfield | ||
| 25℃ | 2750 | cP | Brookfield |
| 25℃ | 55.0 | cP | Brookfield |
| 25℃ | 28000 | cP | Brookfield |
| 25℃ | 95.0 | cP | Brookfield |
| stripping time | 960 to 1400 | min | |
| working hours | |||
| 25℃ | 1.5 to 2.0 | hr |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part C, 77°F |
| 3. Part B, 77°F |
| 4. Part A, 77°F |
| 5. 1″ depth |
| 6. Die B |
| 7. Part A |
| 8. Part C |
| 9. Mixed |
| 10. Part B |
| 11. 1 lb. mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |