| BDF2602AP is a medium viscosity curative incorporated fluoroelastomer copolymer. This is a general purpose grade, well suited for application where excellent process property is required. BDF2602AP can be compounded to meet the major fluoroelastomer specifications. BDF2602AP can be used for compression molding of O-rings, gaskets or oil seals or extrusion molding of articles. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods.&& |
| Product Description | |
|---|---|
| Supplier | Fluoro |
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 38 | MU | |
| Fluorine content | 66 | % | |
| solubility | LMW Ketones and esters | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 76 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 13.8 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 220 | % | ASTM D412 |
| Compression deformation | |||
| 200℃，70 hr | 21 | % | ASTM D395B |
| MH（177℃） | 2.10 | N·m | |
| ML（177℃） | 0.260 | N·m | |
| t’90（177℃） | 2.0 | min | |
| ts2（177℃） | 1.2 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 3. MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |