Boltaron 9815P

About
Boltaron 9815P is a proprietary, fire retardant, extruded PVC/Acrylic alloy that is offered in unlimited surface textures and unlimited colors, providing designers with new ways to enhance the appearance of aircraft interior components. Because it is press laminated (not extruded), unlimited custom textures are available economically in low minimums with fast turnarounds, allowing the production of prototypes and limited runs prior to full-scale production. In addition, the sheet exhibits exceptional physical properties, most notably Izod impact resistance of 5.0 ft lbs/in (265 J/m), significantly improving the durability of thermoformed aircraft interior components, while meeting stringent FAA requirements for flammability, smoke generation and heat release. It also offers extreme formability and consistent surface quality, free of pits or inclusions. Boltaron 9815P is one of the latest additions to Boltaron’s 9815 family of aircraft-rated sheet products specified by the world’s leading commercial, military and private aircraft and helicopter manufacturers, carriers and interior refurbishing contractors, for thermoformed, fabricated and machined interior components of unequalled durability and appearance.&&

About

Boltaron 9815P is a proprietary, fire retardant, extruded PVC/Acrylic alloy that is offered in unlimited surface textures and unlimited colors, providing designers with new ways to enhance the appearance of aircraft interior components. Because it is press laminated (not extruded), unlimited custom textures are available economically in low minimums with fast turnarounds, allowing the production of prototypes and limited runs prior to full-scale production. In addition, the sheet exhibits exceptional physical properties, most notably Izod impact resistance of 5.0 ft lbs/in (265 J/m), significantly improving the durability of thermoformed aircraft interior components, while meeting stringent FAA requirements for flammability, smoke generation and heat release. It also offers extreme formability and consistent surface quality, free of pits or inclusions. Boltaron 9815P is one of the latest additions to Boltaron’s 9815 family of aircraft-rated sheet products specified by the world’s leading commercial, military and private aircraft and helicopter manufacturers, carriers and interior refurbishing contractors, for thermoformed, fabricated and machined interior components of unequalled durability and appearance.&&

Product Description
Generic	PVC alloy
Material Status	Commercial: Active
Features	The fouling resistance,High impact resistance,Low smoke,Flame Characteristics,Good wear resistance,Solvent resistance
Availabilitys	North America
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.49	g/cm³	ASTM D792
Shrinkage rate
MD	0.50 to 0.70	%

IMPACT	Nominal value	Unit	Test method
Notched impact strength of cantilever beam
23℃	270	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed	76.7	℃	ASTM D648
Linear coefficient of thermal expansion
MD	3.0E-5	1/℃	ASTM D696

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	107		ASTM D785
tensile strength	37.9	MPa	ASTM D638
Bending modulus	2830	MPa	ASTM D790
bending strength	60.0	MPa	ASTM D790

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
NBS smoke density			ASTM F814
Ds，1.5 Min	< 100		ASTM F814
Ds，4 Min	< 200		ASTM F814
exothermic			FAR 25.853
2 Min	< 65	kW·min/m²	FAR 25.853
Peak	< 65	kW/m²	FAR 25.853
—	Pass All

Notes
1. Typical properties: these are not to be construed as specifications.
2. A1, (ii)
3. A1, (i)
4. A1 F, Part IV
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.