| About |
|---|
| RF366MO is a specially modified highly-transparent polypropylene random copolymer with medium melt flow rate. This grade is designed for high-speed injection moulding and contains nucleating and antistatic additives. The improved processability, even at low melt temperature, allows energy savings and faster cycle time. Products originating from this grade have excellent transparency, good organoleptic properties, good balance of stiffness and impact strength at ambient temperatures. These properties, together with high gloss, make this grade excellent choice for household and packaging articles. RF366MO can be also used in injection stretch blow moulding (ISBM). RF366MO is intended for injection moulding applications requiring excellent transparency Thin wall packaging Houseware containers Caps and closures Sweet-boxes Cosmetics Appliances Baby bottles Special Features: Outstanding optical properties Improved gloss and excellent transparency Very good processability Good organoleptic properties&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good Clarity,Good surface appearance,High impact resistance,Renewable resources,Optical performance,Nucleation,Good sensory characteristics.,Moderate liquidity,Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.0 to 2.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 29.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 11 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | Internal Method | ||
| 1 µm | 4.0 | % | Internal Method |
| 2 µm | 10 | % | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 260 | °C | |
| Mold temperature | 30 to 40 | °C | |
| Injection speed | Fast | ||
| Hold pressure | 20.0 to 50.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |