| About |
|---|
| Borcoat EB133E-1199-LT is an elastomer modified compound, based on polypropylene copolymer. It has excellent low temperature impact resistance. The product is coloured white. It includes a combination of stabilisers to ensure long-term thermal stability. The product is supplied in pellet form Applications Borcoat EB133E-1199-LT is recommended as a top coat for multilayer PP systems and thermal insulation used in: Steel Pipe Coating Specifications Borcoat EB133E-1199-LT is intended to fulfil following National and International standards, when appropriate industrial manufacturing standard procedures are applied and a continuous quality system is implemented and when used in combination with Borcoat™ BB122E-LT and a compatible powder epoxy. ISO 21809-1 DIN 30678 NF A49-711 Gazprom 2-2.2-178-2007 Due to the nature of the modified PP material, indentation resistance of the applied coating could be borderline versus some requirements of common standards and due to known variations in testing, those specified values should be separately agreed upon between the applicator and the client (end user/purchaser). Special Features Borcoat EB133E-1199-LT is intended for design temperatures between -20°C and +110°C and tailored for low temperature handling, transportation and installation.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Renewable resources,low-temperature impact resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.915 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, F50 | > 3000 | hr | ASTM D1693A |
| Moisture | < 0.050 | % | Karl Fisher |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 60 | ISO 868 | |
| Tensile modulus | |||
| 1 mm | 1000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | > 20.0 | MPa | ISO 527-2/50 |
| yield | 22.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 400 | % | ISO 527-2/50 |
| yield | 13 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.0 | kJ/m² | ISO 179/1eA |
| -20℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 60 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | > 135 | ℃ | ISO 306/A50 |
| Oxidation induction time | |||
| 220℃ | > 30 | min | ISO 11357 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 200 to 220 | °C | |
| Barrel 2 zone temperature | 200 to 220 | °C | |
| Barrel 3 zone temperature | 200 to 220 | °C | |
| Barrel 4 zone temperature | 200 to 220 | °C | |
| Barrel 5 zone temperature | 200 to 220 | °C | |
| Melt temperature | 200 to 240 | °C | |
| Nozzle temperature | 200 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compound |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |