| About |
|---|
| Borcoat ME3000FC is a maleic anhydride grafted polyethylene compound. It includes a combination of pigments and stabilisers to ensure long-term thermal stability. The product is supplied as pellets for melt extrusion. The product is coloured yellow. Applications Borcoat ME3000FC is recommended for melt extrusion of field joint coatings, repair patches and for hot applied tapes/sheets on buried or submerged pipelines. Steel Pipe Coating Specifications Borcoat ME3000FC is intended to fulfil the following international standard: ISO 21809-3, FJC type 5E Special Features Borcoat ME3000FC is a reactive top coat polyethylene compound that can be hot applied directly onto an epoxy pre-coated pipe or as a hot applied tape/sheet together with the powder adhesive Borcoat TM ME0433 .&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Renewable resources,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.934 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 10% non-ionic surfactant | > 5000 | hr | ASTM D1693A |
| humidity | < 500 | ppm | ISO 15512 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| peel strength | |||
| 23℃ | > 20.0 | kN/m | |
| 80℃ | > 5.0 | kN/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -80.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | |||
| A50 | 105 | ℃ | ISO 306/A50 |
| Melting temperature | 121 | ℃ | ISO 11357-3 |
| Oxygen sensing time | |||
| 210℃ | > 30 | min | ISO 11357-6 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | > 25 | kV/mm | ASTM D149 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second | 53 | ISO 868 | |
| tensile strength | |||
| Yield, 23 ℃ | 13.0 | MPa | |
| Fracture, 23 ℃ | 16.0 | MPa | |
| Tensile strain | |||
| Fracture, -45 ℃ | > 100 | % | |
| Fracture, 23 ℃ | > 600 | % |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 170 to 200 | °C | |
| Barrel 2 zone temperature | 170 to 200 | °C | |
| Barrel 3 zone temperature | 170 to 200 | °C | |
| Barrel 4 zone temperature | 170 to 200 | °C | |
| Barrel 5 zone temperature | 170 to 200 | °C | |
| Melt temperature | 190 to 200 | °C | |
| Nozzle temperature | 200 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compound |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |