| About |
|---|
| Borcom WG140AI is a polypropylene microcomposite intended for injection moulding. This material has an excellent balance between impact strength and stiffness, high melt flow rate and gives a good surface quality. Applications Borcom WG140AI has been developed especially for applications like: Climate control housings Air ducts Special Features Long term high heat stabilised Excellent surface appearance UL registered under File E108112&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High impact resistance,Renewable resources,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | 1.3 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20 ℃, injection molding | 1.5 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20 ℃, injection molding | 25 | kJ/m² | ISO 179/1eU |
| 23 ℃, injection molding | 70 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20 ℃, injection molding | 1.6 | kJ/m² | ISO 180-1A |
| 23 ℃, injection molding | 3.7 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -20 ℃, injection molding | 16 | kJ/m² | ISO 180/1U |
| 23 ℃, injection molding | 46 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 64.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 155 | ℃ | ISO 306/A50 |
| B50 | 94.0 | ℃ | ISO 306 |
| Melt Energy | 103 | kJ/kg | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Fogging（100℃） | 1.4 | mg | DIN 75201 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| discharge | 50.0 | µgC/g | VDA 277 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, injection molding | 37.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, injection molding | 4.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| injection molding | 2500 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 50.0 | MPa | ISO 178 |
| Ball hardness | |||
| H358/30 | 85.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |