| LE6023 is a black flexible low density copolymer modified polyethylene compound. It is characterized by excellent stress crack resistance and mechanical properties and low-temperature performance in combination with good extrudability. LE6023 contains 2.5% well dispersed furnace black of nominal particle size 20 nanometers in order to ensure excellent weathering resistance.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Low density,Copolymer,High ESCR |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ISO 1183 | ||
| — | 0.934 | g/cm³ | ISO 1183 |
| — | 0.924 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.35 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 10% non-ionic surfactant, F20 | 1000 | hr | IEC 60811-4-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second | 45 | ISO 868 | |
| tensile strength | |||
| yield | > 14.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 600 | % | ISO 527-2/50 |
| Bending modulus | 125 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.50 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 6.0E-3 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 210 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |