| About |
|---|
| FA3227 is a low density polyethylene produced in a high-pressure process. FA3227 is a Low Density Polyethylene for Film Extrusion, UV stabilised. This grade is suitable for building and construction film and meets the requirements for heat, alkali and UV resistance described in the building standards from the Nordic countries. A 150-micron film based upon FA3227 will last at least four times as long as an unstabilised film of the same thickness. CAS-No.: 9002-88-4 Applications FA3227 has been developed especially for applications like: Construction films Shrink film Heavy-duty sack Liners Additives FA3227 is UV stabilised.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Alkali resistant,Renewable resources,High pressure heat resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| With oneself – dynamic | 0.60 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 130 | µm | |
| Membrane puncture energy | |||
| 130 µm | 5.00 | J | ASTM D5748 |
| Secant modulus | |||
| TD，130 µm | 190 | MPa | ASTM D882A |
| MD，130 µm | 190 | MPa | ASTM D882A |
| tensile strength | ISO 527-3/22 | ||
| MD，24℃，130 µm | 25.0 | MPa | ISO 527-3/22 |
| TD，24℃，130 µm | 23.0 | MPa | ISO 527-3/22 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 130 µ m | 400 | % | ISO 527-3 |
| TD, fracture, 130 µ m | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 130 µm | 450 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：130 µm | 5.0 | N | ISO 6383-2 |
| TD：130 µm | 6.0 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 110 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |