| FG5223 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes Antioxidant and Anti-block additives. This grade is developed for production of lamination film. FG5223 has good heat sealing properties and hot tack strength. By mixing with FG5224 any desired level of friction can be obtained.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High anti-blocking,Thermal viscous strength,Inoxidizability,Butylene copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| With oneself – dynamic | 0.70 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 70 | µm | |
| Secant modulus | |||
| TD，70 µm | 165 | MPa | ASTM D882A |
| MD，70 µm | 145 | MPa | ASTM D882A |
| tensile strength | ISO 527-3 | ||
| MD，70 µm | 29.0 | MPa | ISO 527-3 |
| TD，70 µm | 28.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 70 µ m | 800 | % | ISO 527-3 |
| TD, fracture, 70 µ m | 1000 | % | ISO 527-3 |
| Drop hammer impact | |||
| 70 µm | 260 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：70 µm | 2.0 | N | ISO 6383-2 |
| TD：70 µm | 9.0 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 122 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，70 µm | 100 | ASTM D2457 | |
| Haze | |||
| 70.0 µm | 10 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 220 to 230 | °C | |
| Notes |
|---|
| 1. Silica |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |