| About |
|---|
| BJ100HP is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection moulding process as well as in combination with LGF concentrates on the injection moulding process. The product is available in natural colour. Applications BJ100HP has been developed especially for applications like: Front end carriers Dashboard carriers Under body shieldings Battery supports Door module carriers Special Features BJ100HP is equipped with an additive package for optimum coupling between polymer matrix and glass fibres. The interaction leads to optimum stiffness and impact strength of the components Long term high heat stabilised&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Low Viscosity,Chemical coupling,Copolymer,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.904 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 90 | g/10min | ISO 1133 |
| Shrinkage rate | 1.7 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 1300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, injection molding | 25.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| injection molding | 1250 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 35.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 2.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20 ℃, injection molding | 41 | kJ/m² | ISO 179/1eU |
| 23 ℃, injection molding | 75 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20 ℃, injection molding | 2.5 | kJ/m² | ISO 180-1A |
| 23 ℃, injection molding | 3.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 90.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 150 | ℃ | ISO 306/A |
| — | 72.0 | ℃ | ISO 306/B |
| Melt Energy | 105 | kJ/kg | ISO 11357 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 3.00 to 6.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |