Borealis PP BJ368MO

About
BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borealis Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. Applications Thin wall containers Special Features stiffness and impact balance Good flow behaviour Reduced cycle time and increased output&&

About

BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borealis Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. Applications Thin wall containers Special Features stiffness and impact balance Good flow behaviour Reduced cycle time and increased output&&

Product Description
Supplier	Borealis AG
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Nucleation,Quick molding cycle,Good stripping performance,Copolymer,Antistatic property
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	70	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1500	MPa	ISO 527-2/50
tensile strength
yield	25.0	MPa	ISO 527-2/50
Tensile strain
yield	4.0	%	ISO 527-2/50
Bending modulus	1400	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	3.5	kJ/m²	ISO 179/1eA
23℃	5.5	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature	100	℃	ISO 75-2

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	210 to 260	°C
Mold temperature	10 to 30	°C
Injection speed	Fast
Hold pressure	20.0 to 50.0	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.