Borealis PP BJ380MO

About
BJ380MO is a very high melt flow heterophasic copolymer with high/medium impact strength and stiffness. This grade is designed for high-speed injection moulding and contains nucleating and antistatic additives. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Components moulded from this grade have good demoulding properties and combine good stiffness, gloss and antistatic properties with good low-temperature impact strength. CAS-No. 9010-79-1&&

About

BJ380MO is a very high melt flow heterophasic copolymer with high/medium impact strength and stiffness. This grade is designed for high-speed injection moulding and contains nucleating and antistatic additives. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Components moulded from this grade have good demoulding properties and combine good stiffness, gloss and antistatic properties with good low-temperature impact strength. CAS-No. 9010-79-1&&

Product Description
Supplier	Borealis AG
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,Low warping,High impact resistance,Nucleation,Quick molding cycle,Good stripping performance,Block Copolymer,Weight distribution,Antistatic property,low-temperature impact resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	80	g/10min	ISO 1133
Shrinkage rate	1.0 to 2.0	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
injection molding	1300	MPa	ISO 527-2/50
tensile strength
Yield, injection molding	25.0	MPa	ISO 527-2/50
Tensile strain
Yield, injection molding	5.0	%	ISO 527-2/50
Bending modulus	1200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	3.5	kJ/m²	ISO 179/1eA
23℃	5.0	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	90.0	℃	ISO 75-2/B

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	210 to 260	°C
Mold temperature	20 to 50	°C
Injection speed	Fast
Hold pressure	20.0 to 50.0	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.