| HC205TF is a special nucleated polypropylene homopolymer intended for thermoforming packaging. Its increased crystallisation temperature allows reduced cycle time and increased output Products originating from this grade have excellent transparency, good organoleptic properties, good balance of stiffness and impact strength at ambient temperatures. Applications HC205TF is recommended for: In line and off line thermoforming High transparent trays, cups and containers Housewares and thin wall packaging Margarine tubs and dairy containers Blending with copolymers for lids Special features HC205TF is optimised to deliver: Excellent processability Reduced cycle time and increased output Broad application window Consistent shrinkage behaviour after forming Excellent clarity Very good stiffness and impact balance High gloss Excellent transparency Excellent organoleptic properties&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good Clarity,Good surface appearance,High impact resistance,Crystal,Nucleation,Quick molding cycle,Good sensory characteristics.,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1750 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 35.5 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 8.0 | % | ISO 527-2/50 |
| Bending modulus | 1700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, injection molding | 5.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 106 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 164 to 168 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0,20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |