| About |
|---|
| HF700SA is a polypropylene homopolymer intended for injection moulding. This material has excellent balanced mechanical properties and is easy to process. Applications HF700SA has been developed especially for applications like: Household applications Special Features UL registered under File E108112 High heat stabilised Excellent flowability Excellent antistatic performance&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity,Antistatic property,Heat Stabilized,Homopolymer,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent density | 0.50 to 0.60 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 21 | g/10min | ISO 1133 |
| Shrinkage rate | 1.5 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 15 | kJ/m² | ISO 179/1eU |
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 53.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 94.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 153 | ℃ | ISO 306/A50 |
| B50 | 90.0 | ℃ | ISO 306 |
| Ball indentation temperature | 125 | ℃ | IEC 60695-10-2 |
| Relative temperature index | |||
| Electrical performance, 2.00 mm | 120 | ℃ | UL 746 |
| Strength mechanical performance, 2.00 mm | 120 | ℃ | UL 746 |
| Impact mechanical performance, 2.00 mm | 120 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.00 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，2 µm | 70 | DIN 67530 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 34.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 8.0 | % | ISO 527-2/50 |
| Rockwell hardness | |||
| R-level | 102 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 70.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Hopper temperature | 40 to 80 | °C | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |