| About |
|---|
| HK030U is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection moulding process as well as in combination with LGF concentrates on the injection moulding process. The product is available in standard black 9502.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Renewable resources,noise reduction,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 350 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 0.80 | kJ/m² | ISO 179/1eA |
| -20℃ | 0.90 | kJ/m² | ISO 179/1eA |
| 23℃ | 1.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 11 | kJ/m² | ISO 179/1eU |
| 23℃ | 45 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 1.6 | kJ/m² | ISO 180-1A |
| 23℃ | 1.8 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 53.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 91.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 151 | ℃ | ISO 306/A |
| — | 89.0 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1 mm | 1550 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 33.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2/50 |
| Bending modulus | 1450 | MPa | ISO 178 |
| bending strength | 43.0 | MPa | ISO 178 |
| Ball hardness | 72.0 | MPa | ISO 2039-1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |