| About |
|---|
| RA130E is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is natural coloured. Applications RA130E is recommended for the production of PP-R pipes and fittings used in Heating Plumbing Domestic water Relining Industrial applications The product is used for single as well as for multilayer pipes, where you then differentiate between plastic multilayer and aluminium multilayer pipes. Specifications RA130E is intended to fulfill following standards and regulations, in case of appropriate industrial manufacturing standard procedures applied and a continuous quality system is implemented. DIN 8078 DIN 8077 EN ISO 15874 Special features RA130E is a ready made compound in pellet form for the production of pipes and fittings and included is a specially selected additive package to ensure: Enhanced processability Economical pipe production Excellent product consistency High temperature resistance Low influence on taste & odour Good impact strength The pipe system will show high durability, no corrosion, good weldability, homogeneous joints, low tendency to incrustrations and fast and easy installation.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low liquidity,High impact resistance,Renewable resources,Corrosion Resistant,High Heat Resistance,Low odor,High molecular weight,Random copolymer,Durability,Welding |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.25 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 14 | % | ISO 527-2/50 |
| Bending modulus | 800 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 2.0 | kJ/m² | ISO 179/1eA |
| 0℃ | 3.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 40 | kJ/m² | ISO 179/1eU |
| 0℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD：0~70℃ | 1.5E-4 | 1/℃ | DIN 53752 |
| Thermal conductivity coefficient | 0.24 | W/m/K | DIN 52612 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 180 to 210 | °C | |
| Barrel 2 zone temperature | 180 to 210 | °C | |
| Barrel 3 zone temperature | 180 to 210 | °C | |
| Barrel 4 zone temperature | 180 to 210 | °C | |
| Barrel 5 zone temperature | 180 to 210 | °C | |
| Melt temperature | 220 | °C | |
| Nozzle temperature | 210 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |