| About |
|---|
| SR533 is a polypropylene compound intended for injection moulding. Applications SR533 has been developed especially for the car industry to be used in automotive exterior parts. Bumpers Special features Good stiffness and impact balance Good impact performance for low temperature applications&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low to no calcium content |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 40 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 54.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | 100 | mm/min | ISO 3795 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 56 | ISO 868 | |
| Rockwell hardness | |||
| R-level | 70 | ISO 2039-2 | |
| tensile strength | |||
| Yield, 23 ℃ | 20.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 5.0 | % | ISO 527-2/50 |
| Bending modulus | 800 | MPa | ISO 178 |
| bending strength | 21.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |