| About |
|---|
| Borlink LE0595 is a crosslinkable black polyethylene compound, specially designed for semiconductive conductor screen and bonded insulation screen of energy cables. Borlink LE0595 is designed for semiconductive screens in XLPE medium and high voltage cables. It can be used as inner and outer screen for bonded cable construction and as inner screen for strippable cable constructions. Borlink LE0595 meets the applicable requirements as below when processed using sound extrusion practices and testing procedures AEIC CS8 AEIC CS9 BS 6622 DIN VDE 0276-263 DIN VDE 0276-620 Cenelec HD 620 S1 Cenelec HD 632 S1 IEC 60502-2 IEC 60840 ICEA S-93-639 ICEA S-94-649 ICEA S-97-682 ICEA S-108-720 NF C33-223 NF C33-226 Borlink LE0595 is a ready-to-use semiconductive compound. It offers excellent thermal stability which provides robust cable extrusion and crosslinking at high surface temperature, allowing for high line speed. The excellent distribution of carbon black and additives in Borlink LE0595 results in a smooth semiconductive screen.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | XLPE |
| Material Status | Commercial: Active |
| Features | Conductive,Crosslinked,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| water content | 200 | ppm | Karl Fisher |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 22.0 | MPa | ISO 527-2/25 |
| Tensile strain | |||
| fracture | 200 | % | ISO 527-2/25 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 60811-507 | ||
| Elongation under load: 0.20 MPa, 200 ℃ | 25 | % | IEC 60811-507 |
| Permanent deformation: 0.20 MPa, 200 ℃ | 0.0 | % | IEC 60811-507 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change in Tensile Properties（After Ageing 168 h，135℃） | < 20 | % | IEC 60811-401 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ISO 3915 | ||
| 23℃ | < 1.0E+2 | ohms·cm | ISO 3915 |
| 90 ℃ | < 1.0E+3 | ohms·cm | ISO 3915 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Monsanto ODR | 61.0 | dNm | ASTM D2084 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 4.0 | hr | |
| Melt temperature | 120 to 135 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |