| About |
|---|
| RD208CF is a random copolymer This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications RD208CF is recommended for: Food packaging Lamination films Textile packaging film Stationary films Flower packaging&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,Good heat sealing,High impact resistance,Quick molding cycle,Random copolymer,Soft |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 to 0.910 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23 ℃, injection molding | 650 | MPa | ISO 178 |
| friction coefficient | |||
| With oneself – dynamic | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Membrane puncture force | 1180 | N | ISO 7765-2 |
| Tensile modulus | ISO 527-3 | ||
| MD | 350 to 450 | MPa | ISO 527-3 |
| TD | 350 to 450 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD | 30.0 to 50.0 | MPa | ISO 527-3 |
| TD | 25.0 to 45.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture | 550 to 750 | % | ISO 527-3 |
| TD, fracture | 550 to 750 | % | ISO 527-3 |
| Dart impact equipped with measuring instruments | |||
| Total Energy | 23.0 | J | ISO 7765-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 122 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 138 to 142 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，50 µm | > 120 | ASTM D2457 | |
| Haze | < 1.8 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |