| About |
|---|
| BorShape FX1001 is a blown film grade. It is a high alpha olefin terpolymer polyethylene film grade combining very good extrusion behaviour and superior mechanical properties, which are kept in cold conditions BorShape FX1001 has been developed especially for applications requiring high toughness at high stiffness levels.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | LPE Copolymer |
| Material Status | Commercial: Active |
| Features | Renewable resources,Terpolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.931 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.0kg | 20 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| dynamic | 0.40 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | ||
| MD | 350 | MPa | ISO 527-3 |
| TD | 450 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD | 50.0 | MPa | ISO 527-3 |
| TD | 40.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture | 450 | % | ISO 527-3 |
| TD, fracture | 700 | % | ISO 527-3 |
| Drop hammer impact | 480 | g | ISO 7765-1 |
| Dart impact equipped with measuring instruments | 28.0 | J | ISO 7765-2 |
| Pant tear resistance | ISO 6383-1 | ||
| MD | 60.0 | N/mm | ISO 6383-1 |
| TD | 250 | N/mm | ISO 6383-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 127 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 7 | ASTM D2457 | |
| Haze | 80 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Base Resin |
| 3. Total Penetration Energy |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |