| About |
|---|
| Borstar FB4230 is a linear low density polyethylene film grade combining good and flexible extrusion behaviour, excellent draw down and superior mechanical properties. Blown film extrusion with Borstar LLDPE is comparable to LDPE, but with better flexibility in film thickness range and draw down. Applications Borstar FB4230 has been developed especially for applications like: Food packaging General packaging Pouches Frozen food packaging Additives Borstar FB4230 contains antioxidant.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good dissection,Inoxidizability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.40 | g/10min | ISO 1133 |
| 190℃，21.6kg | 44 | g/10min | ISO 1133 |
| 190℃，5.0kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| With oneself – dynamic | 0.40 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 40 µ m, blow molded film | 300 | MPa | ISO 527-3 |
| TD, 40 µ m, blow molded film | 350 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, 40 µ m, blow molded film | 50.0 | MPa | ISO 527-3 |
| TD, 40 µ m, blow molded film | 40.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 500 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 750 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 180 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：40.0 µm | 70.0 | kN/m | ISO 6383-2 |
| TD：40.0 µm | 200.0 | kN/m | ISO 6383-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart impact equipped with measuring instruments | |||
| Total Penetration Energy，40.0 µm | 150 | J/cm | ISO 7765-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 124 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20 °, 40 µ m, blow molded film | 10 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 70 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |