BR® 127 - SOLIAO

About
BR® 127 corrosion inhibiting primer is a modified epoxy primer. It is the industry standard for high- performance corrosion inhibiting primers and has been used in virtually every commercial aircraft built since its introduction. BR 127 primer can be used with essentially all 250°F (121°C) film adhesives and has been designed to provide optimal structural performance at temperatures ranging from -67°F to 300°F (-55°C to 149°C). BR 127 primer is formulated to provide maximum environmental resistance and durability within the bond line, as well as prevent corrosive undercutting. It can also be used effectively as a protective coating outside bonded areas. BR 127 corrosion inhibiting primer can be cured prior to bonding. Recommended cure cycles range from 4 hours at 180°F (82°C) to 30 minutes at 250°F (121°C). Articles primed with BR 127 primer and then cured have an indefinite shelf life. Primed details should be wrapped in Kraft paper (as protection from dust and dirt) and stored prior to adhesive bonding. Maintaining controlled conditions of 85°F (29°C) maximum temperature and 65% maximum humidity is recommended for extended storage life. Cure cycles for adhesive films primed with BR 127 primer may vary from 200°F to 350°F (93°C to 177°C) with minimum pressures to assure proper mating of bonded details.&&

About

BR® 127 corrosion inhibiting primer is a modified epoxy primer. It is the industry standard for high- performance corrosion inhibiting primers and has been used in virtually every commercial aircraft built since its introduction. BR 127 primer can be used with essentially all 250°F (121°C) film adhesives and has been designed to provide optimal structural performance at temperatures ranging from -67°F to 300°F (-55°C to 149°C). BR 127 primer is formulated to provide maximum environmental resistance and durability within the bond line, as well as prevent corrosive undercutting. It can also be used effectively as a protective coating outside bonded areas. BR 127 corrosion inhibiting primer can be cured prior to bonding. Recommended cure cycles range from 4 hours at 180°F (82°C) to 30 minutes at 250°F (121°C). Articles primed with BR 127 primer and then cured have an indefinite shelf life. Primed details should be wrapped in Kraft paper (as protection from dust and dirt) and stored prior to adhesive bonding. Maintaining controlled conditions of 85°F (29°C) maximum temperature and 65% maximum humidity is recommended for extended storage life. Cure cycles for adhesive films primed with BR 127 primer may vary from 200°F to 350°F (93°C to 177°C) with minimum pressures to assure proper mating of bonded details.&&

Product Description
Supplier	Cytec Industries
Generic	环氧树脂
Material Status	Commercial: Active
Features	Weather resistance is good,Corrosion Resistant,Inoxidizability,Durability,Heat Stabilized
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.875	g/cm³

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.