| The HD3000N is a High Density Polyethylene, narrow molecular weight homopolymer, produced by solution process for Cast film extrusion. It offers high processability, stiffness and good impact resistance. It contains fenol free antioxidant additive.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Inoxidizability,Weight distribution |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.3 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 20.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 380 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 770 | % | ASTM D882 |
| Bending modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 790 | MPa | ASTM D790 |
| 1% secant, MD, 25 µ m, blow molded film | 710 | MPa | ASTM D790 |
| tear strength | |||
| TD, 25 µ m, blow molded film | 10 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 5.0 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 25.0 µ m, blow molded film | 52 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 47 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |