| About |
|---|
| HE150 resin is a High Density Polyethylene that has been specially designed for monofilament extrusion process and provides a good balance of processability, spinnability, knotting strength as well as a very low gels amount. It can also be blended with LLDPE to improve blown film stiffness. Applications: Raschel; shading and protecting nets; ropes; films. Additives: Processing aid additive. Process: The optimum processing conditions vary with the type of equipment used in the production.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low speed solidification point,Food contact compliance,Inoxidizability,Copolymer,High density,Butylene copolymer,Low to no calcium content |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 62 | ASTM D2240 | |
| tensile strength | |||
| Fracture, molded | 40.0 | MPa | ASTM D638 |
| Yield, molding | 28.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 1280 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 76.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 128 | ℃ | ASTM D1525 2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |