| About |
|---|
| HS5103M is a high molecular weight high-density polyethylene, copolymer. Suitable for large parts blow molded an L-ring drum. Exhibit a good impact resistance and excellent stress cracking resistance (ESCR). Applications: L-ring drum and general large parts blow molded. Process: Blow Molding.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Negative |
| Features | High impact resistance,High molecular weight,Copolymer,High ESCR |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 3.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50 | 500 | hr | ASTM D1693 |
| 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 | > 800 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, molded | 35.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 1200 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| -40℃ | No Break | J/m | ASTM D6110 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 70.0 | ℃ | ASTM D648 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compression Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |