Braskem PE LF321FC

About
LF321FC is a Linear Low Density Polyethylene produced by gas phase process, specially developed for XLPE silane cross-linking in monosil process, to use in insulation and jacketing for low voltage wires and cables. This product contains suitable additives, low oligomer rate and very low gel content. Applications: Recommended to cross-linking monosil process, to insulation and jacketing for low voltage XLPE wires and cables. Process: The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. The optimum processing conditions are 170 – 210°C.&&

About

LF321FC is a Linear Low Density Polyethylene produced by gas phase process, specially developed for XLPE silane cross-linking in monosil process, to use in insulation and jacketing for low voltage wires and cables. This product contains suitable additives, low oligomer rate and very low gel content. Applications: Recommended to cross-linking monosil process, to insulation and jacketing for low voltage XLPE wires and cables. Process: The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. The optimum processing conditions are 170 – 210°C.&&

Product Description
Supplier	Braskem
Generic	Linear low density polyethylene
Material Status	Commercial: Negative
Features	Crosslinked,Low speed solidification point
Availabilitys	Latin America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.919	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	2.7	g/10min	ASTM D1238
ESCR(Environmental Stress Cracking Resistance)
50 ℃, 2.00 mm, 100% non-ionic surfactant, molded	> 1000	hr	ASTM D1693

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	> 1.0E+15	ohms·cm	ASTM D257
Dielectric strength	41	kV/mm	ASTM D149
Dielectric constant
1 kHz	2.20		ASTM D150
Dissipation factor
1 kHz	3.0E-4		ASTM D150

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	50		ASTM D2240
tensile strength
Fracture, molded	23.9	MPa	ASTM D638
Tensile strain
Fracture, molded	2000	%	ASTM D638

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.