| About |
|---|
| The resin ML3600S is a Linear Low Density Polyethylene developed for rotomolding. Applications: Water tanks General purpose parts Technical Characteristics: High stiffness Excellent environmental stress cracking resistance (ESCR) UV and heat stabilization Additives: Weathering resistance UV8 and antioxidants&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Inoxidizability,Low density,Copolymer,Hexene copolymers,High ESCR |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.933 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.7 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50 | 250 | hr | |
| 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 | > 1000 | hr | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Yield, molding | 19.0 | MPa | |
| Fracture, molded | 29.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| Yield, molding | 14 | % | |
| Fracture, molded | > 1000 | % | |
| Bending modulus | |||
| 1% cut, molded | 770 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | ARM | ||
| -40 ℃, 3.2mm, roll forming | 55 | J | |
| -40 ℃, 6.4mm, roll forming | 115 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, molded | 60.0 | ℃ | |
| 1.8 MPa, unannealed, molded | 42.0 | ℃ | |
| Melting peak temperature | 127 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |