Braskem PE SGE7252

About
Braskem PE SGE7252 SGE7252 is a bimodal High Density Polyethylene specially developed for the manufacturing of caps and closures that require high stress cracking resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866.&&Braskem PE SGE7252 SGE7252 is a bimodal High Density Polyethylene specially developed for the manufacturing of caps and closures that require high stress cracking resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Caps and closures. Process: Injection Molding.&&

About

Braskem PE SGE7252 SGE7252 is a bimodal High Density Polyethylene specially developed for the manufacturing of caps and closures that require high stress cracking resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866.&&Braskem PE SGE7252 SGE7252 is a bimodal High Density Polyethylene specially developed for the manufacturing of caps and closures that require high stress cracking resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Caps and closures. Process: Injection Molding.&&

Product Description
Supplier	Braskem
Generic	HDPE
Material Status	Commercial: Active
Features	Renewable resources,Food contact compliance,No BPA,High density,High ESCR
Availabilitys	North America,Latin America,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.952 0.952	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	2.0 2.0	g/10min	ASTM D1238
ESCR(Environmental Stress Cracking Resistance)			ASTM D1693
Molded into shape, F50	15.0	hr	ASTM D1693
50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50	40.0	hr	ASTM D1693
Biobased Content	96	%	ASTM D6866

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	55		ISO 868
tensile strength
Fracture, molded	14.0	MPa	ISO 527-2
Fracture, molded	32.0	MPa	ASTM D638
Yield, molding	26.0	MPa	ISO 527-2
Yield, molding	26.0	MPa	ASTM D638
Tensile strain
Fracture, molded	400	%	ISO 527-2
Fracture, molded	400	%	ASTM D638
Yield, molding	9.0	%	ISO 527-2
Yield, molding	9.0	%	ASTM D638
Bending modulus
Compression Molding	1200	MPa	ISO 178
1% cut, molded	1100	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Notched impact strength of cantilever beam
Compression Molding	5.0	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	72.0	℃	ISO 75-2/B
Vicat Softening Temp	125	℃	ISO 306/A

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.