| The polypropylene is granulated, stabilized normally and in natural appearance. For the production of home appliances, medical devices, technical products, packaging products for the food industry, rough textile, parts for the electrical industry and so on.&& |
| Product Description | |
|---|---|
| Supplier | LUKOIL |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good stability,Homopolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.899 to 0.906 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 to 8.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | > 30.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 1% secant | > 1100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | > 20 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 55.0 | ℃ | ASTM D648 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 3. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |