| The polypropylene is granulated, stabilized normally and in natural appearance. For the production of home appliances, technical parts, car batteries, parts for the electrical and auto industries, packages for the food, wine and tobacco industries.&& |
| Product Description | |
|---|---|
| Supplier | LUKOIL |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Copolymer,Good stability |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.896 to 0.903 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 to 5.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| injection molding | > 23.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 1% cut, injection molding | > 900 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | > 70 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, injection molded | > 49.0 | ℃ | ASTM D648 |
| Embrittlement temperature | > -5.00 | ℃ | ASTM D746 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Procedure A |
| 4. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |