| BYNEL® Series 3000 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. BYNEL 3000 series resins adhere to a wide variety of materials. They are most often used to adhere to PE, ionomers, EVA and polyamide.&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good bond |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.932 | g/cm³ | ASTM D792 |
| Density | 0.932 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.1 | g/10min | ISO 1133 |
| 190℃，2.16kg | 2.1 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 81.0 | ℃ | ASTM D1525 |
| Vicat Softening Temp | 81.0 | ℃ | ISO 306 |
| Melting peak temperature | 99.0 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 99.0 | ℃ | ISO 3146 |
| freezing point | 87 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 135 | °C | |
| Barrel 2 zone temperature | 185 | °C | |
| Barrel 3 zone temperature | 210 | °C | |
| Barrel 4 zone temperature | 235 | °C | |
| Barrel 5 zone temperature | 235 | °C | |
| Connector temperature | 235 | °C | |
| Melt temperature | < 235 | °C | |
| Nozzle temperature | 235 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |