| About |
|---|
| CABELEC CA3896 is an electrically conductive compound based on conductive carbon black dispersed in a modified styrenic resin. The electrical properties are permanent and are not dependent on atmospheric conditions. Applications CABELEC CA3896 has been specially designed for packaging and electronic product handling where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosives, electronic components and pigments.&& |
| Product Description | |
|---|---|
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | Conductive,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | Internal Method |
| Melt Flow Rate | ISO 1133 | ||
| 200℃，10.0kg | 5.0 | g/10min | ISO 1133 |
| 200℃，21.6kg | 38 | g/10min | ISO 1133 |
| 200℃，5.0kg | 1.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 75 | ASTM D2240 | |
| tensile strength | |||
| fracture | 24.3 | MPa | ISO 527-2 |
| yield | 30.4 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 23 | % | ISO 527-2 |
| Bending modulus | 1880 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 16 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 72.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 101 | ℃ | ISO 306/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| 0.4 mm | 2.1E+3 | ohms | Internal Method |
| Volume resistivity | 3.0E+2 | ohms·cm | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 200 | °C | |
| Barrel middle temperature | 200 | °C | |
| Barrel front temperature | 200 | °C | |
| Nozzle temperature | 235 | °C | |
| Mold temperature | 30 | °C | |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 170 to 200 | °C | |
| Barrel 3 zone temperature | 170 to 200 | °C | |
| Barrel 5 zone temperature | 170 to 200 | °C | |
| Melt temperature | < 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |