CABELEC® CA4749

About
CABELEC CA4749 electrically conductive compound is made from carbon black and a copolymer of ethylene and vinyl acetate. This product is suitable for extrusion applications where low resistivity and low flexural modulus are required. Applications CABELEC CA4749 conductive compound is suitable for incorporation into flexible articles such as pipes, tubes, flooring and matting and for applications where it is desirable to mitigate the hazard of electrostatic discharge, such as ordnance and ammunition works, mines and petroleum plants.&&

About

CABELEC CA4749 electrically conductive compound is made from carbon black and a copolymer of ethylene and vinyl acetate. This product is suitable for extrusion applications where low resistivity and low flexural modulus are required. Applications CABELEC CA4749 conductive compound is suitable for incorporation into flexible articles such as pipes, tubes, flooring and matting and for applications where it is desirable to mitigate the hazard of electrostatic discharge, such as ordnance and ammunition works, mines and petroleum plants.&&

Product Description
Generic	EVA
Material Status	Commercial: Active
Features	Good flexibility,Conductive,Copolymer
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.14	g/cm³	Internal Method
Melt Flow Rate			ISO 1133
190℃，10.0kg	0.10	g/10min	ISO 1133
190℃，21.6kg	4.0	g/10min	ISO 1133
Shrinkage rate
MD	2.0 to 2.3	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 15 seconds	51		ASTM D2240
tensile strength
fracture	14.6	MPa	ISO 527-2
yield	14.6	MPa	ISO 527-2
Tensile strain
fracture	260	%	ISO 527-2
Bending modulus	220	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	43.0	℃	ISO 75-2/B
Vicat Softening Temp	75.0	℃	ISO 306/A

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	50	ohms	Internal Method
Volume resistivity	5.0	ohms·cm	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	75	°C
Drying time	2.0 to 4.0	hr
Barrel 1 zone temperature	150 to 170	°C
Barrel 3 zone temperature	150 to 170	°C
Barrel 5 zone temperature	150 to 170	°C
Melt temperature	< 210	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.