| About |
|---|
| CALIBRE™ 201-6 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity as well as high melt strength for sheet extrusion applications. The CALIBRE 200-6 series products are available in 4 additive packages: CALIBRE 200: No mold release or UV Stabilizer. CALIBRE 201: Mold release. CALIBRE 202: UV stabilizer. CALIBRE 203: Mold release and UV stabilizer. . (Note that CALIBRE 202 and 203 grades are not available in Europe and do not comply with EU food contact regulations). Govt. And Industry Standards: U.S. FDA 21 CFR 177.1580 CSA Underwriters Laboratory (UL) EU food contact 2011/10/EC Applications Small & large appliances Beverage containers/service ware Liquid containers Food processor housings Custom sheet Packaging applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,Food contact compliance,Good melt strength |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.60 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| 23℃，50% RH | 0.32 | % | ASTM D570 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 6.0 | g/10min | ASTM D1238 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.59 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze μ M | 1.0 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 142 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 129 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 151 | ℃ | ASTM D1525 | |
| Linear coefficient of thermal expansion | |||
| MD | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+15 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 12 | KV/mm | ASTM D149 | |
| Dielectric constant | |||
| 23℃ | 3.00 | 1 MHz | ASTM D150 |
| Dissipation factor | |||
| 23℃ | 2.0E-3 | 1 MHz | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | V-2 | UL 94 | |
| 1.50mm | V-2 | UL 94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 910 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 73 | M 级 | ASTM D785 |
| Rockwell hardness | 118 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 120 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 2410 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 96.5 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2410 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 260-280 | °C | |
| Central temperature of the barrel | 270-290 | °C | |
| Barrel front temperature | 280-300 | °C | |
| Die temperature | 280-300 | °C | |
| Mold temperature | 80-100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 2.0 in/min |
| 4. Method I (3 point load), 0.079 in/min |
| 5. 0.079 in/min |
| 6. 11.1 ft/sec |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 8. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |