| About |
|---|
| CALIBRE™ 2061-12 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-12 provides exceptional clarity, heat resistance, impact strength, processability, and has low contamination levels. CALIBRE 2061-12 resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release. Main Characteristics: ISO 10993 Applications: Medical applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,High purity,High impact resistance,Steam sterilized,Biocompatible,Ethylene oxide disinfection,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| 300℃，1.20kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23℃ | 46 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 65 | kJ/m² | ISO 180-A |
| 23℃ | 750 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D256 | |
| Notched impact strength of cantilever beam | |||
| 23℃ | No Break | ISO 180 | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 82.2 | J | ASTM D3763 |
| Tensile impact strength | 378 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 136 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 129 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 130 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 126 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 140 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 147 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 2.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2220 | MPa | ASTM D638 |
| Tensile modulus | 2200 | MPa | ISO 527-2/50 |
| tensile strength | |||
| fracture | 73.7 | MPa | ISO 527-2/50 |
| yield | 62.9 | MPa | ISO 527-2/50 |
| yield | 62.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| fracture | 150 | % | ISO 527-2/50 |
| yield | 6.0 | % | ISO 527-2/50 |
| yield | 6.0 | % | ASTM D638 |
| Bending modulus | 2220 | MPa | ASTM D790 |
| Bending modulus | 2250 | MPa | ISO 178 |
| bending strength | 99.2 | MPa | ASTM D790 |
| bending strength | 92.5 | MPa | ISO 178 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 73 | ASTM D785 | |
| R-level | 118 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Method I (3 point load), 0.079 in/min |
| 4. 0.079 in/min |
| 5. 3-points |
| 6. 11.1 ft/sec |
| 7. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |