| About |
|---|
| CALIBRE™ 2061-6 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-6 provides excellent heat resistance, impact strength, and processability. CALIBRE 2061-6 resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release and is currently available in black color. Main Characteristics: Tested under ISO 10993 Applications: Medical applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Steam sterilized,High Heat Resistance,Ethylene oxide disinfection,HB,V-2 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 850 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D256 | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 89.3 | J | ASTM D3763 |
| Tensile impact strength | |||
| 23℃ | 567 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 142 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 129 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 145 | ℃ | ASTM D648 |
| Vicat Softening Temp | 156 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.00 mm | HB | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2410 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 68.3 | MPa | ASTM D638 |
| yield | 62.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| yield | 6.0 | % | ASTM D638 |
| Bending modulus | 2410 | MPa | ASTM D790 |
| bending strength | 96.5 | MPa | ASTM D790 |
| Taber abraser | 45 | % | ASTM D1044 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 73 | ASTM D785 | |
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 25 | % | |
| Barrel rear temperature | 271 to 288 | °C | |
| Barrel middle temperature | 277 to 299 | °C | |
| Barrel front temperature | 299 to 327 | °C | |
| Nozzle temperature | 299 to 327 | °C | |
| Processing (melt) temperature | 299 to 327 | °C | |
| Mold temperature | 77 to 110 | °C | |
| Screw speed | 40 to 70 | rpm | |
| Clamping force | 2.8 to 6.9 | kN/cm² | |
| Screw length to diameter ratio | 15.0:1.0 | ||
| Screw compression ratio | 1.5:1.0 to 3.0:1.0 | ||
| Notes |
|---|
| 1. Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Dow for details. ISO guidelines include a sensitization test. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 2.0 in/min |
| 4. Method I (3 point load), 0.079 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |