| About |
|---|
| CALIBRE ™ 300 series are general purpose grades. These grades have a good balance of heat resistance and impact resistance. This series include some modified versions for better mold release property and weather resistant property, thus this series could cover a broad range of applications including extruded sheets, electronic parts, stationery, mobile equipment and other miscellaneous applications.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Negative |
| Features | Good stripping performance,V-2 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 22.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| TD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 60 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 740 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 139 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 134 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 126 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD | 7.0E-5 | 1/℃ | ASTM D696 |
| TD | 7.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | ASTM D149 |
| Arc resistance | 110 | sec | ASTM D495 |
| Compared to the leakage tracing index | 300 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.44 mm | V-2 | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.585 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| Tensile modulus | 2300 | MPa | ISO 527-2 |
| tensile strength | |||
| — | 62.0 | MPa | ASTM D638 |
| — | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D638 |
| fracture | 110 | % | ISO 527-2 |
| Bending modulus | |||
| — | 2200 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 89.0 | MPa | ASTM D790 |
| — | 85.0 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |