| About |
|---|
| CALIBRE™ 300V-10 Series polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. The CALIBRE 300V series products are available in 2 additive packages: CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mold release and UV stabilizer. Products may be offered in colors. Please check for availability. Complies with: CSA (Canadian Standards Association) Underwriters Laboratory, Inc. (UL) Consult the regulations for complete details. Applications: Electronic components Lighting Storage media housings&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,V-2 |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 , ISO 1183/B |
| Melt Flow Rate | |||
| 10 | g/10min | ASTM D1238 | |
| 300℃，1.20kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | ISO 62 |
| balance | 0.32 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2410 | MPa | ASTM D638 |
| — | 2300 | MPa | ISO 527-2/50 |
| tensile strength | ASTM D638 , ISO 527-2/50 | ||
| yield | 60.0 | MPa | ASTM D638 , ISO 527-2/50 |
| fracture | 71.0 | MPa | ASTM D638 , ISO 527-2/50 |
| Tensile strain | ASTM D638 , ISO 527-2/50 | ||
| yield | 6.0 | % | ASTM D638 , ISO 527-2/50 |
| fracture | 150 | % | ASTM D638 , ISO 527-2/50 |
| Bending modulus | |||
| — | 2410 | MPa | ASTM D790 |
| — | 2400 | MPa | ISO 178 |
| bending strength | |||
| — | 97.0 | MPa | ISO 178 |
| yield | 96.5 | MPa | ASTM D790 |
| Taber abraser | 45.0 | mg | ASTM D1044 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| — | 910 | J/m | ASTM D256 |
| 23℃ | 35 | kJ/m² | ISO 180-4A |
| Notched impact strength of cantilever beam | 无断裂 | ASTM D256 , ISO 180 | |
| Dart impact equipped with measuring instruments | 87.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 141 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa, unannealed | 125 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 122 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 138 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 143 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 146 | ℃ | ASTM D1525 , ISO 306/B50 |
| Ball pressure temperature | 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149，IEC 60243-1 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | 1.0E-3 | ASTM D150 | |
| Compared to the leakage tracing index | |||
| 2.00 mm, solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | |||
| — | 1.586 | ASTM D542 | |
| — | 1.586 1.586 | ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |