| CALIBRE™ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Glass reinforced Ignition resistant Tested under ISO 10993 Applications Information Technology Equipment Telecommunications Medical applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Biocompatible,Flame Characteristics,V-2,V-0 |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Density | 1.27 | g/cm³ | ISO 1183/B |
| Density | 1.27 | g/cm³ | ISO 1183-3 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| 300℃，1.20kg | 15 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ISO 294-4 |
| MD | 0.20 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | ASTM D570 |
| 23℃，24hr | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 3 | |
| -30℃ | No Break | ISO 179/1eU 3 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 80 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 40.1 | J | ASTM D3763 |
| Tensile impact strength | 147 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 134 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 134 | ℃ | ASTM D648 |
| 1.8 MPa | 137 | ℃ | ISO 75-2 3 |
| 0.45 MPa, annealed | 144 | ℃ | ISO 75-2/B |
| 0.45 MPa, annealed | 144 | ℃ | ASTM D648 |
| 0.45 MPa | 147 | ℃ | ISO 75-2 3 |
| Vicat Softening Temp | 160 | ℃ | ASTM D1525 8 |
| B50 | 160 | ℃ | ISO 306 |
| B50 | 148 | ℃ | ISO 306 3 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 3.8E-5 | 1/℃ | ASTM D696 |
| MD | 3.8E-5 | 1/℃ | ISO 11359-2 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Flame retardant level | |||
| 3.20 mm | V-0 | ISO 1210 3 | |
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| Oxygen index | 32 | % | ISO 4589-2 3 |
| Average combustion degree | 1 | cm | ASTM D635 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3380 | MPa | ASTM D638 |
| Tensile modulus | 3380 | MPa | ISO 527-2/50 |
| Tensile modulus | 3600 | MPa | ISO 527-2 3 |
| tensile strength | |||
| fracture | 61.0 | MPa | ISO 527-2/50 |
| fracture | 60.7 | MPa | ASTM D638 |
| yield | 62.0 | MPa | ISO 527-2/50 |
| yield | 60.0 | MPa | ISO 527-2 3 |
| yield | 62.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 6.0 | % | ASTM D638 |
| fracture | 6.0 | % | ISO 527-2/50 |
| yield | 4.0 | % | ISO 527-2 3 |
| Nominal strain at break | 10 | % | ISO 527-2 3 |
| Bending modulus | 3170 | MPa | ASTM D790 |
| Bending modulus | 3170 | MPa | ISO 178 |
| bending strength | 93.8 | MPa | ASTM D790 |
| bending strength | 94.0 | MPa | ISO 178 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 62 | ASTM D785 | |
| R-level | 122 | ASTM D785 |
| Notes |
|---|
| 1. Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4. 2,0 in/min |
| 5. Method I (3 point load), 0,079 in/min |
| 6. 0,079 in/min |
| 7. 11,1 ft/sec |
| 8. Rate A (50°C/h), Loading 2 (50 N) |
| 9. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |