| About |
|---|
| CALIBRE™ MEGARAD™ 2080-15 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to high energy radiation (gamma or electron beam), CALIBRE MEGARAD 2080-15 resin can reduce the color shift by 50% compared to general purpose polycarbonate resins. CALIBRE 2080-15 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Stabilized for higher energy radiation Tested under ISO 10993 Transparent Contains no mold release Applications: Medical applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Negative |
| Features | Good Clarity,E-beam disinfection,Biocompatible,Radiation disinfection |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 , ISO 1183/A |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| Water absorption rate | ASTM D570 , ISO 62 | ||
| 23℃，24hr | 0.15 | % | ASTM D570，ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ASTM D570，ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 25 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 750 | J/m | ASTM D256 |
| 23℃ | 75 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ASTM D256 , ISO 180 | |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, total energy | 81.3 | J | ASTM D3763 |
| Tensile impact strength | 378 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 139 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 122 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 136 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 148 | ℃ | ASTM D1525 7 |
| B50 | 143 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 , ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| Tensile modulus | |||
| — | 2210 | MPa | ASTM D638 |
| — | 2300 | MPa | ISO 527-2/50 |
| tensile strength | |||
| yield | 62.1 | MPa | ASTM D638 |
| yield | 62.0 | MPa | ISO 527-2/50 |
| fracture | 68.3 | MPa | ASTM D638 |
| fracture | 68.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 150 | % | ASTM D638 |
| fracture | 150 | % | ISO 527-2/50 |
| Bending modulus | |||
| — | 2410 | MPa | ASTM D790 |
| — | 2400 | MPa | ISO 178 |
| bending strength | |||
| — | 96.5 | MPa | ASTM D790 |
| — | 98.0 | MPa | ISO 178 |
| Wear resistance | 45 | % | ASTM D1044 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Method I (3 point load), 0.079 in/min |
| 4. 0.079 in/min |
| 5. 3-points |
| 6. 11.1 ft/sec |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |