| About |
|---|
| Caltex PP HT42 is a Polypropylene material. It is available in Asia Pacific. Important attributes of Caltex PP HT42 are: Flame Rated Heat Resistant High Stiffness Typical applications include: Appliances Automotive Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | GS Caltex |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03-1.07 | g/cm³ | ISO 1183 |
| ash content | 18-22 | % | ISO 3451-1A |
| Melt Flow Rate | |||
| 9.0-15 | g/10min | ISO 1133 | |
| Volatiles | 0.15 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 140 | ℃ | ISO 75-2/Af |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 1.65mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 29.4 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 100 | R 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 34 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 15 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2705 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |