| CAPILENE® G 71 TF is a nucleated polypropylene homopolymer intended for sheet extrusion and thermoforming applications requiring improved transparency and higher stiffness than conventional polypropylene. CAPILENE® G 71 TF features: nucleated, high stiffness, high clarity, good thermal stability, short molding cycle. Applications CAPILENE® G 71 TF is suitable for: transparent trays, food containers, food packaging and cups.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Nucleation,Heat Stabilized,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 38.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 9.0 | % | ASTM D638 |
| Bending modulus | 2100 | MPa | ASTM D790 |
| Bending modulus | 2000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180 |
| 23℃ | 30 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 122 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 110 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 159 | ℃ | ASTM D1525 4 |
| Vicat Softening Temp | 159 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 1000 µm | 25 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.20 in/min |
| 4. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |