| CAPRAN® 980 is a clear (low haze level), heat-stabilized cast film produced from modified nylon 6 resin. It is recommended as bagging film for advanced composite fabrication and other high temperature applications where dimensional stability, adherence to sealant tapes and uniform film gauge are essential. CAPRAN® 980 has excellent heat stability and resistance to pinholing. It can be used at temperatures up to 390oF (199oC) for typical composite cure cycle times.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good Dimensional Stability,Heat Stabilized |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| film | Nominal value | Unit | Test method |
| film thickness | |||
| test | 51 | µm | |
| Secant modulus | |||
| MD，51 µm | 552 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 51 µ m | 31.0 | MPa | ASTM D882 |
| MD, fracture, 51 µ m | 112 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture, 51 µ m | 380 | % | ASTM D882 |
| Elmandorf tear strength | |||
| MD，51 µm | 130 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Crystallization peak temperature | |||
| DSC | 218 to 220 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |