| About |
|---|
| Modified Ethylene Copolymer CAPXIDAN™ HD is a Modified Copolymer produced with a proprietary, specialized formulation. It is designed to be coextruded over Wood-Plastic Composite (WPC) deck boards to provide moisture, stain, wear resistance, aesthetics, durability at elevated temperatures, and unprecedented adhesion to the WPC substrate. CAPXIDAN™ HD is a two-component capstock system. The CAPXIDAN™ resin should be extruded together with a specific synergistic additive masterbatch in the recommended proportion of 98:2 by weight.&& |
| Product Description | |
|---|---|
| Generic | Ethylene copolymer |
| Material Status | Commercial: Active |
| Features | The fouling resistance,Good bond,Moisture resistance,Copolymer,Good wear resistance,Durability |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| -40℃ | 2310 | MPa | ISO 527-2 |
| 0℃ | 1690 | MPa | ISO 527-2 |
| 23℃ | 862 | MPa | ISO 527-2 |
| tensile strength | ASTM D638 | ||
| yield | 20.0 | MPa | ASTM D638 |
| fracture | 21.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 400 | % | ASTM D638 |
| Bending modulus | ISO 178 | ||
| -40℃ | 517 | MPa | ISO 178 |
| 0℃ | 379 | MPa | ISO 178 |
| 23℃ | 207 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD：-100~85℃ | 1.5E-4 | 1/℃ | ASTM D696 |
| specific heat | |||
| 23℃ | 1920 | J/kg/℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |