| Celanex 2002 is a general purpose, unreinforced polybutylene terephthalate with a good balance of mechanical properties and processability. Celanex 2002 is a medium flow material.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Moderate liquidity,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 20 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| MD | 1.8 to 2.0 | % | ASTM D955 |
| TD | 1.8 to 2.0 | % | ISO 294-4 |
| MD | 1.8 to 2.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.19 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 190 | kJ/m² | ISO 179/1eU |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| Glass transition temperature | 60.0 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| B50 | 190 | ℃ | ISO 306 |
| Melting peak temperature | 225 | ℃ | ASTM D3418 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 1.4E-4 | 1/℃ | ISO 11359-2 |
| MD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric strength | 23 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.4E-3 | IEC 60250 | |
| 1 MHz | 0.022 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.70 mm | HB | UL 94 | |
| Extreme oxygen index | 22 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ASTM D638 | ||
| -40℃ | 3100 | MPa | ASTM D638 |
| 23℃ | 3170 | MPa | ASTM D638 |
| 80℃ | 469 | MPa | ASTM D638 |
| 121℃ | 296 | MPa | ASTM D638 |
| Tensile modulus | 2600 | MPa | ISO 527-2/1A/1 |
| tensile strength | ASTM D638 | ||
| fracture | 35.0 | MPa | ISO 527-2/1A/50 |
| yield | 60.0 | MPa | ISO 527-2/1A/50 |
| 50% strain | 30.0 | MPa | ISO 527-2/1A/50 |
| Yield, -40 ℃ | 101 | MPa | ASTM D638 |
| Yield, 0 ℃ | 75.8 | MPa | ASTM D638 |
| Yield, 23 ℃ | 55.8 | MPa | ASTM D638 |
| Yield, 80 ℃ | 24.8 | MPa | ASTM D638 |
| Yield, 121 ℃ | 17.9 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Fracture, 23 ℃ | 200 | % | ASTM D638 |
| fracture | 220 | % | ISO 527-2/1A/50 |
| yield | 4.0 | % | ISO 527-2/1A/50 |
| Yield, -40 ℃ | 7.2 | % | ASTM D638 |
| Yield, 0 ℃ | 4.4 | % | ASTM D638 |
| Yield, 23 ℃ | 3.2 | % | ASTM D638 |
| Yield, 80 ℃ | 17 | % | ASTM D638 |
| Yield, 121 ℃ | 23 | % | ASTM D638 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2/1A/50 |
| Bending modulus | |||
| 23℃ | 2500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 80.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 78 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 130 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 25 | % | |
| Hopper temperature | 20 to 50 | °C | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 235 to 250 | °C | |
| Nozzle temperature | 250 to 260 | °C | |
| Processing (melt) temperature | 235 to 260 | °C | |
| Mold temperature | 65 to 93 | °C | |
| Injection speed | Moderate-Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |