| About |
|---|
| Chemical abbreviation according to ISO 1043-1: PBT Moulding compound ISO 7792- PBT, MGHR, 08-030N Polybutylene terephthalate, easy flow, nucleated grade Flammability UL 94 HB Minimum thickness 1.0 mm. Recognition by Underwriters Laboratories, USA (UL)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good liquidity,Nucleation,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2700 | MPa | ISO 527-2/1A/1 |
| tensile strength | ISO 527-2/1A/50 | ||
| yield | 60.0 | MPa | ISO 527-2/1A/50 |
| fracture | 60.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 15 | % | ISO 527-2/1A/50 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 2400 | MPa | ISO 899-1 |
| 1000 hr | 1600 | MPa | ISO 899-1 |
| bending strength | |||
| 23℃ | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 130 | kJ/m² | ISO 179/1eU |
| 23℃ | 140 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 190 | ℃ | ISO 306 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 23 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | IEC 60250 | |
| 1 MHz | 3.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.3E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| Extreme oxygen index | 22 | % | ISO 4589-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.8 to 2.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Density of Melt | 1.110 | g/cm³ | Internal Method |
| Specific Heat Capacity of Melt | 1920 | J/kg/℃ | Internal Method |
| Thermal Conductivity of Melt | 0.13 | W/m/K | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 50 | °C | |
| Barrel rear temperature | 240 to 250 | °C | |
| Barrel middle temperature | 240 to 250 | °C | |
| Barrel front temperature | 245 to 255 | °C | |
| Nozzle temperature | 250 to 260 | °C | |
| Processing (melt) temperature | 250 to 260 | °C | |
| Mold temperature | 75 to 85 | °C | |
| Injection pressure | 60.0 to 100 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 30s |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |